The Influences of Drying Temperature of Wood Particles on the Quality Properties of Particleboard Composite


Sari B., NEMLİ G., Ayrilmis N., BAHAROGLU M., Bardak S.

DRYING TECHNOLOGY, cilt.31, sa.1, ss.17-23, 2013 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 31 Sayı: 1
  • Basım Tarihi: 2013
  • Doi Numarası: 10.1080/07373937.2012.711791
  • Dergi Adı: DRYING TECHNOLOGY
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.17-23
  • Anahtar Kelimeler: Chemical properties, Drying temperature, Mechanical properties, Particleboard, Physical properties, Surface roughness, Wettability, HEAT-TREATMENT, SURFACE CHARACTERISTICS, DIMENSIONAL STABILITY, MECHANICAL-PROPERTIES, PHYSICAL-PROPERTIES, MDF PANELS, WETTABILITY, STRENGTH, COLOR
  • Karadeniz Teknik Üniversitesi Adresli: Evet

Özet

The objective of this investigation was to evaluate the effects of drying temperature of wood particles on the quality properties of particleboard composite and chemical properties of wood. Test panels were manufactured using wood particles dried at different temperatures ranging from 100 to 180 degrees C. Based on the findings obtained in this study, increasing drying temperature of the particles negatively affected the mechanical properties, surface roughness, and wettability of the particleboards. However, increasing drying temperature significantly caused a positive effect on the thickness swelling. The results showed that the particleboards made from particles dried at 180 degrees C did not meet the required levels of mechanical strength properties according to the EN 312 (2010) standard for furniture production. The particleboards made from wood particles dried at 150 degrees C for 35 min appeared to be a practical choice for interior fitments.