Copper-based hybrid metal matrix composites reinforced with graphene and zinc were developed to achieve a balanced combination of mechanical strength, corrosion resistance, wear performance, and electrical conductivity. In this study, Cu matrix composites containing a constant graphene content of 1 wt.% and varying Zn contents (0, 5, 10, and 15 wt.%) were fabricated through mechanical alloying followed by Spark Plasma Sintering (SPS). The effects of zinc content on microstructure, densification, hardness, corrosion behavior, tribological performance, and electrical conductivity were systematically investigated. Microstructural analyses revealed that the combined use of graphene and Zn significantly influenced grain refinement, interfacial stability, and densification behavior. The composite containing 10 wt.% Zn exhibited the highest relative density (similar to 90.5%) and maximum hardness (62 HB), indicating an optimal reinforcement level. Corrosion tests conducted in 3.5 wt.% NaCl solution demonstrated that the 10 wt.% Zn composite showed the most noble corrosion potential and the lowest corrosion current density, which was attributed to reduced porosity and improved microstructural homogeneity. Tribological results confirmed that graphene contributed to a self-lubricating effect, while Zn enhanced load-bearing capacity, leading to improved wear resistance under increasing normal loads. Electrical conductivity measurements showed a gradual decrease with increasing Zn content, mainly due to solid-solution-induced electron scattering in the Cu matrix; however, the fixed graphene addition and effective SPS consolidation helped preserve conductive pathways, allowing all composites to retain acceptable conductivity levels. The results indicate that the hybrid Cu-graphene-Zn composites exhibit a balanced combination of mechanical, corrosion, tribological, and electrical properties, with 10 wt.% Zn emerging as the optimal composition.