Production of dissolving grade pulp from poplar wood by ethanol-water process, 26, 239-245


KIRCI H., Akgül M.

TURKISH JOURNAL OF AGRICULTURE AND FORESTRY, vol.26, pp.239-245, 2002 (Peer-Reviewed Journal)

  • Publication Type: Article / Article
  • Volume: 26
  • Publication Date: 2002
  • Journal Name: TURKISH JOURNAL OF AGRICULTURE AND FORESTRY
  • Journal Indexes: Scopus, TR DİZİN (ULAKBİM)
  • Page Numbers: pp.239-245

Abstract

The possibilities of dissolving grade pulp production from poplar by an ethanol-water process were investigated. The effects of ethanol ratio, cooking temperature and acid catalyst ratio on unbleached, bleached and alkali-purified pulps were studied.

It was seen that catalyst ratios exceeding 0.01% caused serious yield and viscosity losses. The results showed that with the catalyst ratio to pulping liquor exceeding 0.01%, pulp yield and viscosity were reduced to an unacceptable level. The best pulping result wasobtained at 40% ethanol consistency, 180 ºC pulping temperature and 150 min reaction time without the addition of acid catalyst to the pulping liquor. After bleaching and alkali purification, the pulp obtained had a 30.7% yield, 95.8% α-cellulose content, 677 cm3 /g viscosity, 83% ISO brightness, 1.80% residual pentosans, 0.33% copper number and 0.14% ash content. However, brightness was increased to 88.5% ISO level with the application of a multistage bleaching (CEHDED) sequence instead of chlorite bleaching without serious losses in yield or α-cellulose content at normal viscosity levels. It is concluded that these pulps meet dissolving grade pulp quality requirements