Roasting of Celestite in Laboratory Scale Rotary Furnace


Ertürk S., Sezer R., Hızlı İ. G., Bilen A., Arslan C.

8th International Symposium on High-Temperature Metallurgical Processing, California, Amerika Birleşik Devletleri, 26 Şubat - 02 Mart 2017, ss.469-476 identifier identifier

  • Yayın Türü: Bildiri / Tam Metin Bildiri
  • Cilt numarası:
  • Doi Numarası: 10.1007/978-3-319-51340-9_46
  • Basıldığı Şehir: California
  • Basıldığı Ülke: Amerika Birleşik Devletleri
  • Sayfa Sayıları: ss.469-476
  • Anahtar Kelimeler: Turkish celestite, Roasting, PRECIPITATION, WATER, SRCO3, SRS
  • Karadeniz Teknik Üniversitesi Adresli: Evet

Özet

Turkish celestite ore was roasted in a lab scale rotary kiln furnace with metallurgical coke. Coke and celestite were mixed; the product contained 32% coke which is more than the stoichiometric requirement. 100 g of the mixed product was fed to a rotary furnace at 35 g/min. Temperature (1000 and 1100 degrees C), rotation speed (2.5, 5 and 10 rpm) and the slope of the furnace (2, 3 and 5 degrees) were among the investigated parameters. Phase and chemical analyses were carried out by XRD and XRF techniques, respectively. The maximum solubility of the roasted product in water was 48% under the roasting conditions of 1100 degrees C, 2.5 rpm and 2 degrees slope.