Limited oxygen index levels of impregnated Scots pine wood

Tomak E. D., Cavdar A. D.

THERMOCHIMICA ACTA, cilt.573, ss.181-185, 2013 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 573
  • Basım Tarihi: 2013
  • Doi Numarası: 10.1016/j.tca.2013.09.022
  • Dergi Adı: THERMOCHIMICA ACTA
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.181-185
  • Anahtar Kelimeler: Scots pine, Boron, Fire retardancy, Oxygen index, THERMAL-DEGRADATION, MECHANICAL-PROPERTIES, BORIC-ACID, FLAME RETARDANTS, FIRE RESISTANCE, COMPOSITES, COMBUSTION, PYROLYSIS
  • Karadeniz Teknik Üniversitesi Adresli: Evet

Özet

In this study, effect of various concentrations of boron powder, mixture of boric acid and borax, fireproof agent based on liquid blend of limestone, and silicon oil on limited oxygen index levels (LOI) of S. pine wood was investigated. Wood samples were first vacuum treated with the preservatives, and then were subjected to leaching procedure. Samples treated with fireproof agent showed the best results for improving the fire retardancy of wood, furthermore, samples treated with 25%, 50% and 100% of the solution did not burn. Leaching did not considerably change the LOI of wood samples treated with boron powder and silicon oil; however, LOI levels of samples treated with the mixture of boric acid and borax and fireproof agent were affected by leaching procedure probably arising those preservatives did not chemically bond to main wood components. All treatments improved fire retardancy of samples despite some amount of preservatives leached out from wood. (C) 2013 Elsevier B.V. All rights reserved.