Structural, Optical and Electrochromic Properties of WO<sub>3</sub> Thin Films Prepared by Chemical Spray Pyrolysis Versus Spin Coating Technique

MORKOÇ KARADENİZ, SİBEL; İSKENDEROĞLU, Demet; ERTUĞRUL, MEHMET; EKİNCİ, ALİ

doi:10.3964/j.issn.1000-0593(2018)09-2982-07

Structural, Optical and Electrochromic Properties of WO<sub>3</sub> Thin Films Prepared by Chemical Spray Pyrolysis Versus Spin Coating Technique

Atıf İçin Kopyala

MORKOÇ KARADENİZ S., İSKENDEROĞLU D., ERTUĞRUL M., EKİNCİ A. E.

SPECTROSCOPY AND SPECTRAL ANALYSIS, cilt.38, sa.9, ss.2982-2988, 2018 (SCI-Expanded)

Yayın Türü: Makale / Tam Makale
Cilt numarası: 38 Sayı: 9
Basım Tarihi: 2018
Doi Numarası: 10.3964/j.issn.1000-0593(2018)09-2982-07
Dergi Adı: SPECTROSCOPY AND SPECTRAL ANALYSIS
Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
Sayfa Sayıları: ss.2982-2988
Karadeniz Teknik Üniversitesi Adresli: Hayır

Özet

In this study, Tungsten Oxide (WO3) thin films were prepared by Chemical Spray Pyrolysis (CSP) and Spin Coating (SC) techniques and it was investigated effects of technique and parameter on the films. WO3 thin films were deposited on ITO (Indium Tin Oxide) coated glasses. The structural, optical and electrochromic properties of the WO3 thin films were characterized by XRD, SEM, UV, and CV measurements. The sharpest (200) peak was observed in the XRD spectra and optical band gaps were calculated around 2.6 similar to 3.1 eV via UV-Vis spectra for all of the samples. Micro fibrous reticulated surface (filamentous like) morphology for the films deposited by CSP technique and smooth surface morphology with high optical transmittance for the film deposited by SC Technique were obtained from SEM images. In addition to these results, it was revealed that all the samples exhibit good electrochromic performance.